Liquid Sprayed Decorative Aluminium Sheet Custom Surface Treatment
Thickness 2.0 Mm
Liquid-sprayed solid aluminum sheet is used aluminum or aluminum
alloy as the raw material, the processing of molding and decorative
surface protective and decorative coating of architectural aluminum
cladding. The use of internationally renowned brands of the United
States PPG, Japan's state legislature fluorocarbon coating company,
the PVDF content of not less than 70 percent, to ensure that the
color and durability of excellent quality. Our production of
fluorocarbon liquid sprayed aluminum sheet by the State Building
Materials Quality Supervision and Inspection Center testing,
product performance in full compliance with "building decorative
aluminum sheet," the national standards.
Product specifications:
Aluminum dimensions: thickness 2.0 mm, 2.5 mm, 3.0 mm, 4.0 mm, 5.0
mm, 6.0 mm
Width :1000mm-1900mm length: ≤ 6000mm
Finished products size: Machinable molding length ≤ 6000mm, width ≤
1500mm, height ≤ 1.9mm.
Special Size: Conventional circular plate forming radius ≥ 150mm
Special can make modle.
Punching hole punching aperture ≤ 80mm hole shape, size, spacing
can be customized according to customer requirements.
Board Effect:
Test Data:
| Test item | Requirements of standard | Result |
| Film thickness | Average≥40μm Min. ≥34μm | Average 45μm Min.38μm |
| Dry-film hardness | ≥1H | 2H |
| Gloss value | Gloss value＜30 | Tolerance±5 | Gloss value26.9-31.2 average28.6 |
| ＜30 Gloss value＜30 | Tolerance±7 |
| Gloss value≥70 | Tolerance±10 |
| Impact resistance | both the aluminum should be no crack. Coating without loss and
craze | both the aluminum no crack. Coating without loss and craze |
| Film adhesion | Drying adhesion | Class0 | Class0 |
| Wet adhesion | Class0 | Class0 |
| Boiling water adhesion | Class0 | Class0 |
| Hydrochloric acid resistance | No change | No change |
| Nitric acid resistance | No changes such as blistering,△E≤5.0 | No changes such as blistering,△E=5.0 |
| Mortar resistance | No change | No change |
| Solvent resistance | No base exposed | No base exposed |
| Salt spray resisitance(4000h) | No lower than grader 1 | Class1 |
| Humidity resistance(4000h) | No lower than grader 1 | Class1 |
| (4000h)artificial weathering | Colour retention | △E≤3.0 | 0.6 |
| Gloss retention | ≥70% | 89% |
| Others | No lower than grader 1 | Class0 |